Properties | Units | 95%Alumina | 99 % Alumina | ZrO2 |
Density | g / cm³ | 3.7 | 3.92 | 5.95-6.0g/cm³ |
Water absorption | % | 0 | 0 | 0 |
Coefficient of thermal expansion | 10-6/K | 7.9 | 8.5 | 10.5 |
Modulus of Elasticity Young's Mod | GPa | 280 | 340 | 210 |
Poisson's ratio | / | 0.21 | 0.22 | 0.3 |
HV Hardness HV | MPa | 1400 | 1650 | 1300-1365 |
Flexural Strength @ room temperature | MPa | 280 | 310 | 950 |
Flexural Strength @700°C | MPa | 220 | 230 | 210 |
Compressive Strength @ room temperature | MPa | 2000 | 2200 | 2000 |
Fracture Toughness | MPa *m 1/2 | 3.8 | 4.2 | 10 |
Heat conductivity @ room temperature | W/ m*k | 18-25 | 26-30 | 2-2.2 |
Electrical Resistivity @ room temperature | Ω*mm2 /m | >1015 | >1016 | >1015 |
Max use temperature | °C | 1850 | 2100 | 1650 |
Resistance to acid alkaline | / | high | high | high |
Dielectric Constant | / | 9.5 | 9.8 | 26 |
Dielectric Strength | KV/mm | 10 | 10 | 10 |
Thermol Shock Resistance | △ T ( °C ) | 220 | 180-200 | 280-350 |
Tensile Strength @ 25 °C | MPa | 200 | 248 | 252 |
Thermal Conductivity(25℃) | W/m·K | 30 | 35 | 3 |
Dynamic information Ceramic technology FAQ Ceramice exhibition
Ceramics quality Ceramics technical Ceramice after-sale Customer witness Patent certificate
Ceramic flange Ceramic bushing Ceramic plunger Ceramic pump valve